Bound phosphorus-modified zeolite catalyst, method of preparing and method of using thereof

ABSTRACT

Disclosed is a bound phosphorus-modified zeolite catalyst. Zeolite is treated with a phosphorus compound to form the phosphorus-treated zeolite. Binder material is treated with a mineral acid prior to being bound with the phosphorus-modified zeolite. The binder material includes inorganic oxide materials, such as alumina, clay, aluminum phosphate and silica-alumina, in particular, a binder of alumina or clay or their combinations. The mineral acid includes hydrochloric acid, nitric acid, phosphoric acid or sulfuric acid. The phosphorus-treated zeolite is combined with the acid-treated inorganic oxide binder material to form a zeolite-binder mixture. Water is added to form an extrudable paste which maybe shaped and is heated to a temperature of about 400° C. or higher to form a bound phosphorus-modified zeolite catalyst. For aromatic alkylation, the bound phosphorus-modified zeolite catalyst is contacted with an aromatic alkylation feed of an aromatic compound and an alkylating agent under reaction conditions suitable for aromatic alkylation.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates generally to the alkylation of aromatic compoundsand catalysts used for such reactions and their preparation.

2. Description of the Prior Art

Before 1940 virtually all of the aromatic solvents, including xylene,were produced from coal. Thereafter production of xylene from petroleumstarted. Most mixed xylene is currently produced by catalytic reformingof petroleum aromatic-rich streams from refineries. It is also obtainedfrom pyrolysis gasoline as a by-product of olefin manufacture during thecracking of hydrocarbons, by-product of naphtha cracking. Xylene canalso be obtained from toluene by disproportionation or alkylation.Toluene disproportionation (TDP) is a catalytic reaction of toluene toproduce xylenes and benzene. Toluene methylation (TM) is a catalyticreaction of toluene with methanol to produce xylenes as shown below:

All of these processes generally produce a mixture of isomers. Thexylene isomers, meta-xylene (m-xylene), ortho-xylene (o-xylene) andpara-xylene (p-xylene), are important chemical intermediates. o-Xyleneis oxidized to make phthalic anhydride which is used to make phthalateplasticizers among other things. m-Xylene is oxidized to makeisophthalic acid, which is used in unsaturated polyester resins (UPR).However, p-xylene has by far the largest market of the three isomers.The largest use of p-xylene is in its oxidation to make terephthalicacid. Terephthalic acid is used in turn to make polymers such aspolyethylene terephthalate (PET) and polybutylene terephthalate (PBT).PET is one of the largest volume polymers in the world. As such thedemand for p-xylene is several times that for m- and o-xylene. Incommercial manufacture p-xylene is purified from mixed xylenes bycrystallization and adsorption processes.

Thermodynamic equilibrium compositions of o-, m-, and p-xylenes areapproximately 25, 50 and 25%, respectively, at 500° C. The catalyticprocesses such as TDP and TM would give about 25% p-xylene (PX) inmixed-xylenes (MX). However, if a catalyst possesses shape selectiveproperties it will give significantly greater than 25% PX. Typically, ashape selective catalyst would give >85% PX in MX.

Zeolites are crystalline solids made up of aluminum-substituted SiO₄tetrahedral units joined together to form different ring and cagestructures into a crystalline framework. The physical structure ofzeolite is very porous with a large internal and external surface area.The substitution of aluminum generates a charge imbalance which must becountered by a supplementary counterion, such as a proton.

Zeolites can be shape-selective catalysts due to steric and electroniceffects. Selective reactions can occur over zeolites as certainproducts, reactants or transition states are kept from forming withinthe pores either by transition state selectivity or because of size orshape of molecular diameter. By varying the preparation of zeolitecatalysts, they can be modified to carry out very specific syntheses ofdesired products.

Modified zeolite catalysts are known for alkylation of aromatics,specifically methylation of toluene to xylenes, especially p-xylene

U.S. Pat. No. 6,504,072 discloses a phosphorus-modified zeolite used inthe selective methylation of toluene to p-xylene. The P-modified zeolitecatalyst may contain active and inactive materials such as clays, silicaand/or metal oxides such as alumina as a binder. There is no disclosureof modification or treatment of the binder and no disclosure of theeffect of modification or treatment of the binder on selectivity topara-xylene.

Other prior art discloses the modification or treatment of bindermaterial for zeolite catalysts used in other processes.

U.S. Pat. No. 5,907,073 discloses a process for alkylation of anaromatic with a molecular sieve catalyst of a modified zeolite betahaving an intergrowth of a ZSM-12 crystalline framework. Duringsynthesis, NH₄-Beta and LaNH₄-Beta were mulled with nitric acid treatedalumina, extruded and calcined which converted the NH₄-Beta andLaNH₄-Beta into H-Beta catalyst and LaH-Beta catalyst, respectively. Thefinished catalyst was used in ethylation of benzene to formethylbenzene. There is no disclosure that modification or treatment ofthe binder had an effect on selectivity.

U.S. Pat. No. 5,380,690 discloses a catalyst for the production of lightolefins which is a mixture of clay, inorganic oxides and zeoliteprepared by mixing the precursor of the inorganic oxides such asaluminum sol, pseudo-bohemite, silica sol or its mixture, andsilica-alumina sol or gel with clay, peptizing with de-cationized waterto prepare a slurry, further mixing homogeneously, adjusting andmaintaining the pH value of the slurry to 2-4 using inorganic acid suchas hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid,after aging statically, adding into it a pre-calculated amount ofzeolite, homogenizing, spray drying, washing-off isolated sodium ions,and drying. There is no disclosure that adjusting and maintaining the pHof the slurry containing the binder precursor had an effect onselectivity.

U.S. Pat. No. 6,047,544 discloses an engine exhaust gas purificationcatalyst of a layer of palladium, platinum or rhodium on a layer of azeolite hydrocarbon adsorbent on a monolithic substrate. Duringsynthesis, Pd-impregnated alumina powder, Pd-impregnated cerium oxidepowder, nitric acid acidified alumina sol and water were introduced intoa magnetic ball mill to crush the mixture so as to obtain a slurry. Thenitric acid acidified alumina sol was obtained by adding 10 weight %nitric acid to 10 weight % bemite alumina. There is no disclosure thatmodification or treatment of the alumina had an effect on selectivity.

U.S. Pat. No. 6,399,530 discloses a hydrocracking catalyst having abinder of a small pore alumina which is peptized with nitric acid andhas a specific surface area of 240-280 m²/g and a pore volume of 0.4-0.5ml/g. There is no disclosure that modification or treatment of thealumina binder had an effect on selectivity.

U.S. Pat. No. 6,566,293 discloses an olefin-selective catalyst forproduction of light olefins which is a phosphorus-modified zeolitehaving a binder. The alumina binder is usually peptized before or duringits combination with the other catalyst composition components. There isno disclosure that peptization of the alumina binder was with a mineralacid or that peptization of the alumina binder had an effect onselectivity.

SUMMARY OF THE INVENTION

A bound zeolite catalyst is a zeolite treated with a phosphorus compoundto form a phosphorus-treated zeolite and an inorganic oxide bindermaterial treated with a mineral acid. The catalyst can be made bycombining a phosphorus-treated zeolite with an inorganic oxide bindermaterial which has been treated with a mineral acid to form azeolite-binder mixture and heating the zeolite-binder mixture attemperature of about 400° C. or higher to form a bound zeolite catalyst.The bound phosphorus-modified zeolite catalyst can be used in a processfor alkylation of aromatics, such as methylation of toluene to xylenes,by contacting the bound zeolite catalyst with an aromatic compound andan alkylating agent under reaction conditions suitable for aromaticalkylation.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete appreciation of the invention and many of the associatedand resultant advantages thereof will be readily understood by referenceto the following detailed description when considered in connection withthe accompanying drawings in which like numerals in different figuresrepresent the same structures or elements wherein:

FIG. 1 is a plot of p-xylene selectivity as a function of time on streamfor the toluene methylation reaction for catalysts B of Example 2 andcatalyst F of Example 6;

FIG. 2 is a plot of p-xylene selectivity as a function of time on streamfor the toluene methylation reaction for catalysts M of Example 13 andcatalyst N of Example 14.

DETAILED DESCRIPTION OF THE INVENTION

Toluene methylation is known to occur over zeolite or zeolite-typecatalysts, in particular, ZSM-5-type zeolite catalysts. Generally, athermodynamic equilibrium mixture of ortho (o)-, meta (m)- and para(p)-xylenes is formed from the methylation of toluene. Thermodynamicequilibrium compositions of o-, m-, and p-xylenes may be around 25, 50and 25 mole %, respectively, at a reaction temperature of about 500 ° C.Such toluene methylation may occur over at wide range of temperatures,however.

A high purity grade (99+%) p-xylene is desirable for its oxidation toterephthalic acid process. Thus, an increased concentration of p-xyleneover equilibrium is desirable. However, production cost for such aconcentration can be very high. p-Xylene can be separated from mixedxylenes by cycle of adsorption and isomerization which must be repeatedmany times because of its low isomeric concentration in the equilibriummixture. If the concentration of p-xylene is higher than equilibrium,the high purity grade p-xylene can be more easily attained. An amount ofp-xylene significantly higher than equilibrium can be obtained if thecatalyst contains shape selective properties. Such shape selectiveproperties can be incorporated in zeolite catalyst by modifying thezeolite.

Zeolite is a crystalline hydrated aluminosilicate that may also containother metals, such as sodium, calcium, barium, and potassium, and thathas ion exchange properties (Encarta® World English Dictionary [NorthAmerican Edition]© & (P) 2001 Microsoft Corporation). Examples ofzeolites are ZSM-5, ZSM-11, ZSM-5/ZSM-11 intermediate, ZSM-12, ZSM-21,ZSM-22, ZSM-23, ZSM-35, ZSM-38, ZSM-48, ZSM-50, MCM-22, Zeolite L,Zeolite Beta and Mordenite which are known in the art.

ZSM-5 zeolite is a porous material containing intersectingtwo-dimensional pore structure with 10-membered oxygen rings. Zeoliteswith such 10-membered oxygen ring pore structures are often classifiedas medium-pore zeolites. As used herein, the expression “ZSM-5-type” ismeant to refer to those zeolites that are isostructurally the same asZSM-5 zeolites. Additionally, the expressions “ZSM-5” and “ZSM-5-type”may also be used herein interchangeably to encompass one another andshould not be construed in a limiting sense.

ZSM-5 zeolite catalysts and their preparation are described in U.S. Pat.No. 3,702,886, which is herein incorporated by reference. In the presentinvention, the ZSM-5 zeolite catalyst may include those having asilica/alumina molar ratio of 200 or higher, more particularly fromabout 250 to about 500 prior to modification. The starting ZSM-5 may bean NH₄ ⁻ or H⁺ form and may contain traces of other cations.

Modification of ZSM-5-type zeolite catalysts with phosphorus-containingcompounds has been shown to provide shape selective properties to thecatalyst, yielding significantly greater amounts of p-xylene than thethermodynamic equilibrium value when used in toluene methylationcompared to unmodified catalysts. Such modification has been shown toprovide selectivity for p-xylenes of greater than 80%.

The ZSM-5 may be modified by treating with phosphorus-containingcompounds including, but are not limited to, phosphonic, phosphinous,phosphorus and phosphoric acids, salts and esters of such acids andphosphorous halides. In particular, phosphoric acid (H₃PO₄) and ammoniumhydrogen phosphate ((NH₄)₂HPO₄) may be used as the phosphorus-containingcompound to provide a catalyst for toluene methylation with shapeselective properties to provide increased p-xylene selectivity. Suchmodified catalysts may contain phosphorus (P) in an amount of from about0.01 to about 0.15 g P/g zeolite, more particularly from about 0.02 toabout 0.13 g P/g zeolite, and more particularly from about 0.07 g P/gzeolite to about 0.12 g P/g zeolite, and still more particularly fromabout 0.09 g P/g zeolite to about 0.11 g P/g zeolite. After phosphorustreatment, the phosphorus-treated zeolite may be dried.

The phosphorus-modified ZSM-5 may be made by forming a slurry of aZSM-5-type zeolite and an aqueous solution of a phosphorus compound andremoving water from the slurry to form a phosphorus-modified ZSM-5zeolite. The phosphorus-modified catalyst prepared as described inPublished U.S. Patent Application 20050239635 (STC-03-0006) publishedOct. 27, 2005, which is herein incorporated by reference, is not steamedand has a pore volume of from 0.2 ml/g or less.

The phosphorus-modified ZSM-5 may be made by dissolving alumina in aphosphorus-containing acid solution and treating the zeolite with thedissolved alumina solution as described in U.S. Pat. No. 6,943,131issued Sep. 13, 2005, which is herein incorporated by reference.

The phosphorus-modified ZSM-5 may have particular ³¹P MAS NMR peaksindicating the present of free phosphate, phosphate bonded toextra-framework aluminum, or particular phosphate species as describedin U.S. Ser. No. 11/136,877 (STC-04-0023) filed May 25, 2005, which isherein incorporated by reference.

Zeolites other than ZSM-5 which are useful in the present invention aremedium pore zeolites that have 10 and/or 12 member ring channels system,such as ZSM-4 (Zeolite Omega), ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZeoliteBeta, Mordenite, MCM-22 and combinations and mixtures thereof.Silica-alumina phosphates (SAPO), aluminum phosphates (AlPO) andcombinations and mixtures thereof are also useful in the presentinvention.

The phosphorus-modified zeolite may be heated at 300 ° C. or higherafter phosphorus treatment and then combined with an inorganic oxidebinder material to form a zeolite-binder mixture which forms a boundzeolite catalyst as described in U.S. Ser. No. 11/195,970 (STC-05-0001)filed Aug. 3, 2005, which is herein incorporated by reference.

In the present invention, the phosphorus-modified zeolite is combinedwith a binder material which has been treated with a mineral acid or asolution of a mineral acid. The binder material includes inorganic oxidematerials, such as alumina, clay, aluminum phosphate and silica-alumina.In particular, a binder of alumina or clay or their combinations isparticularly useful.

When used in aromatic alkylation, especially toluene methylation, abound phosphorus-modified zeolite catalyst which has had the inorganicbinder material treated with a mineral acid, such as hydrochloric acid,nitric acid, phosphoric acid or sulfuric acid, before combining thebinder material with the phosphorus-modified zeolite will provideincreased selectivity to p-xylene. In addition, a phosphorus-modifiedzeolite catalyst bound with an inorganic binder material which has beentreated with a mineral acid will produce toluene methylation productwith relatively lower C9+ content. Also, a phosphorus-modified zeolitecatalyst bound with an inorganic binder material which has been treatedwith a mineral acid will be more resistant to catalyst attrition asmeasured by crush strength.

The inorganic binder material is treated with a mineral acid by adding asufficient amount of the mineral acid to form a mixture between theinorganic binder material and the liquid mineral acid in which there isno excess liquid.

After forming the mixture between the inorganic binder material and themineral acid, the phosphorus-modified zeolite is mixed into the mixtureand water is added to form a paste which can be extruded to from ashaped catalyst precursor. The catalyst precursor is calcined to form abound zeolite catalyst at a temperature of 400° C. or higher, moreparticularly at a temperature between 500° C. and 700° C. Such heatingmay be carried out for 0.5 hours or more to form the bound catalyst. Thebound catalyst may contain from about 1% to about 99% binder by totalweight of bound catalyst, more particularly from about 10% to about 50%binder by total weight of bound catalyst.

The bound P-modified zeolite catalyst may be mildly steamed at atemperature of 300° C. or lower before using the catalyst in anyreaction. The steaming can be carried out in-situ or ex-situ of thereactor. The use of catalyst steaming at mild temperatures is describedin co-pending U.S. patent application Ser. No. 11/122,919 (STC-04-0021),filed May 5, 2005, entitled “Hydrothermal Treatment ofPhosphorus-Modified Zeolite Catalysts,” which is herein incorporated byreference.

The bound P-modified ZSM-5 catalyst may be contacted with an appropriatefeed of an aromatic hydrocarbon and an alkylating agent under alkylationreaction conditions to carry out aromatic alkylation. The catalyst hasparticular application for use in toluene methylation utilizing atoluene/methanol feed. A gas cofeed may also be used. The cofeed gas mayinclude hydrogen or an inert gas. As used herein, the expression“alkylation feed” is meant to encompass the aromatic compound and thealkylating agent. As used herein, the expression “methylation feed” ismeant to encompass the feed of toluene and methanol.

In addition to any cofeed gas, water that may be in the form of steam,may also be introduced into the reactor as cofeed along with thealkylation feed. The water or steam used for the methylation reactionmay be introduced with or without hydrogen or inert gas as cofeed withthe alkylation feed to the reactor during the start up of the alkylationreaction, or it may be introduced subsequent to initial start up. Ineither case, liquid water may be added and vaporized prior to its mixingwith cofeed gas (if any) and the alkylation feed. The use of watercofeed is described in U.S. Patent App. Publication No. US2005/0070749A1 (STC-03-0008)), published Mar. 31, 2005, and entitled “TolueneMethylation Process,” and in U.S. Ser. No. 11/127,357 (STC-04-0016)filed May 12, 2005, as a continuation-in-part application entitled“Toluene Methylation Process with Increased Methanol Selectivity”, bothof which are herein incorporated by reference.

The reactor pressure for toluene methylation or other aromaticalkylation may vary, but typically ranges from about 10 to about 1000psig. Reactor temperatures may vary, but typically range from about 400to about 700° C. Upon introduction of feed into the reactor, thecatalyst bed temperature may be adjusted to a selected reactiontemperature to effect a desired conversion. The temperature may beincreased gradually at a rate of from about 1° C./min to about 10°C./min to provide the desired final reactor temperature. As used in theexamples, reactor temperature refers to the temperature as measured atthe inlet of catalyst bed of the reactor.

The catalyst of the claimed invention may be used in a process fortoluene methylation with a startup procedure in which thetoluene/methanol feed is introduced into the reactor at a relativelyhigh liquid hourly space velocity (LHSV) with a cofeed of hydrogen forone-half to about 20 hours before running the reactor at a relativelylower LHSV as described in U.S. Ser. No. 10/632,254 (STC-03-0004) filedAug. 1, 2003, which is herein incorporated by reference.

The reaction may be carried out in a variety of different reactors thatare commonly used for carrying out aromatic alkylation reactions. Singleor multiple reactors in series and/or parallel are suitable for carryingout the aromatic alkylation. Methanol and/or toluene may be added to theproduct stream entering the second and subsequent reactors when usingmultiple reactors in series.

The P-modified ZSM-5 zeolite catalyst, as described herein, hasparticular application for use in toluene methylation for preparing axylene product from a feed of toluene and methanol. The catalystprovides increased selectivity for p-xylene when used in toluenemethylation. In particular, the catalyst may provide greater than 85%,90% or 95% para-xylene selectivity when used in toluene methylation.Additionally, in certain instances, greater than 95% of total xyleneselectivity may be achieved.

Additionally, the bound P/ZSM-5 catalyst described herein will providesteady catalyst activity and selectivity for toluene methylation overthe same periods of times under appropriate reaction conditions asunbound P/ZSM-5 catalysts and bound P/ZSM-5 in which the inorganicbinder material has not been treated with a mineral acid.

Processes useful for the present invention other than toluenemethylation would include aromatic alkylation and transalkylation,toluene disproportionation, methanol to gasoline (MTG) processes andn-paraffin (C₆ and higher) cyclization.

The invention having been generally described, the following examplesare given as particular embodiments of the invention and to demonstratethe practice and advantages thereof. It is understood that the examplesare given by way of illustration and are not intended to limit thespecification or the claims to follow in any manner. The followingexamples serve only to illustrate and not to limit the invention.

As used herein, catalytic activity can be expressed as the % moles ofthe toluene converted with respect to the moles of toluene fed and canbe defined by the following formulas:

Mole % Toluene Conversion=[(T _(i) −T _(o))/T _(i)]×100   (1)

where, T_(i) is the number of moles of toluene fed and T_(o) is thenumber of moles toluene unreacted. As used herein, selectivity for mixedxylenes may be expressed as:

Mole % Mixed Xylene Selectivity=[X _(tx)/(T _(i) −T _(o))]×100   (2)

where, X_(tx) is the number of moles of mixed (o-, m- or p-) xylenes inthe product.

As used herein, selectivity for p-xylene may be expressed as:

Mole % p-Xylene Selectivity=(X _(p) /X _(tx))×100   (3)

where, X_(p) is the number of moles of p-xylene.

As used herein, methanol conversion may be expressed as:

Mole % Methanol Conversion=[(M _(i) −M _(o))/M _(i)]×100   (4)

where, M_(i) is the number of moles of methanol fed and M_(o) is thenumber of moles methanol unreacted.As used herein, methanol selectivity for toluene methylation may beexpressed as:

Mole % Methanol Selectivity=[X _(tx)/(M _(i) −M _(o))]×100   (5)

where, X_(tx) is the number of moles of mixed (o-, m- or p-) xylenes,M_(i) is the number of moles of methanol fed and M_(o) is the number ofmoles of unreacted methanol.

Example 1 (Comparative) Catalyst A

Synthesis of Catalyst A. A binder free P-modified ZSM-5 (P/ZSM-5) wasmade. The starting zeolite powder was an NH₄-ZSM-5 powder havingSiO₂/Al₂O₃ mole ratio 280. Slurry containing 450.0 g of NH₄-ZSM-5zeolite and 900 ml of water was prepared in a 2-L beaker. The beaker wasplaced on a hot plate and the zeolite slurry was stirred using amechanical (overhead) stirrer with 250-300 rpm. The temperature of theslurry was slowly raised to about 80-85 ° C. at which time phosphoricacid was added slowly. A weighted 205.2 g of phosphoric acid (Aldrich,85 wt % in aqueous) was added into the beaker. The slurry temperaturewas further increased to between 95-100° C. and heating was continueduntil all liquid was evaporated. The phosphoric-acid modified zeolitewas calcined in a convection oven in air at the following temperatureprogram: 90° C. to 120° C. for three hours, at 340° C. to 360° C. forthree hours and at 520° C. to 530° C. under air for 13 hours. Thecalcined zeolite was then crushed and sized using 20 and 40 mesh screensfor catalytic reaction or sieved through 80 mesh screen for binding itwith a suitable binder. The P/ZSM-5 was analyzed for Si, Al and P by XRFmethod, and for BET surface area and total pore volume by N₂ adsorption.As shown in Table 1, the P/ZSM-5 zeolite contained 36.42 wt % Si, 0.27wt % Al and 9.38 wt % P, and it had BET surface area of 154 m²/g andtotal pore volume of 0.12 ml/g. The X-ray diffraction pattern for theP/ZSM-5 was recorded on a Phillips (X'Pert model) diffractometer over arange of 5-55° at a scan rate 2° per minute using CuK_(α1) radiation andresults were given in Table 2.

TABLE 1 Elemental Analysis, wt % N₂ Adsorption Si Al P SA, m²/g PV, ml/g36.42 0.27 9.38 154 0.12

TABLE 2 Powder XRD Intensity* d-spacing [A] Intensity 11.11 100 10.02 579.73 17 8.04 11 6.69 8 6.54 9 6.34 11 5.97 16 5.70 8 5.56 7 4.01 10 3.9313 3.85 51 3.74 19 3.71 29 3.64 10 2.52 25 2.98 9 *Intensities shown arescaled in arbitrary units so that most intense peak is 100.

Catalyst A was used for toluene methylation reaction. The reaction wascarried out in a fixed bed, continuous flow type reactor. A catalystcharge of 5.4 ml (catalyst size: 20-40 mesh) loaded in a SS-316 tube (OD0.5 inch, ID 0.33 inch) reactor. Catalyst was dried by slowly raisingthe catalyst bed temperature (about 5° C./min) to 200° C. under hydrogenflow (50 cc/min) for at least one hour. Catalyst was then steamed byintroducing water vapor (2.2 mmole/min) with a carrier gas of H₂ (459cc/min) at 200 ° C. overnight. A premixed toluene and methanol feed(molar ratio about 4.5) was added to the reactor at 200° C. The liquidhourly space velocity (LHSV) (based on methylation feed) was maintainedat about 2 hr⁻¹ and a cofeed H₂ gas was fed and maintained to provideH2/methylation feed molar ratio of about 7-8. In addition, water wasadded to reactor as cofeed and was vaporized prior to introduction toreactor. The H₂O/methylation feed molar ratio was about 0.8 and reactorpressure was about 20 psig. The catalyst bed inlet temperature wasincreased incrementally to increase toluene conversion. Reactor streamswere analyzed to calculate conversion and selectivity. Product streamswere analyzed. Conversion and selectivity for toluene methylationreaction over catalyst A are shown in Table 3.

TABLE 3 Time on Stream, h 24.10 52.60 119.60 149.77 173.60 198.13 221.60Catalyst Bed Inlet Temp, ° C. 452.3 487.7 495.7 530.3 529.6 531.0 533.7Liquid Product Analysis, wt % Water 19.31 20.07 20.02 19.76 19.01 19.6619.94 Methanol 0.86 0.75 0.66 0.58 0.53 0.56 0.57 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 75.92 72.39 71.11 69.70 69.60 69.0968.88 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 2.95 5.51 6.79 8.51 9.27 9.089.08 m-Xylene 0.35 0.49 0.56 0.62 0.68 0.67 0.67 o-Xylene 0.38 0.46 0.480.49 0.52 0.51 0.50 Ethyltoluenes 0 0.06 0.06 0 0 0 0 Trimethylbenzenes0.22 0.28 0.32 0.34 0.39 0.37 0.37 C10+ 0 0 0 0 0 0 0Conversion/Selectivity, mole % Toluene Conversion 3.09 5.86 7.63 9.4010.24 10.17 10.16 Mixed Xylene Selectivity 94.92 95.51 96.06 97.07 96.9196.60 97.06 p-Xylene Selectivity 80.02 85.42 86.74 88.46 88.52 88.5388.62 Methanol Selectivity 28.98 42.64 50.22 56.90 60.12 60.15 60.52

Example 2 (Comparative) Catalyst B

Synthesis of Catalyst B. P-modified ZSM-5 (described as catalyst Aearlier) was bound with 20 wt % alumina binder. 17.5 g of alumina(pseudobohemite type, available from Alcoa, HiQ-40 grade) was mixed with70.0 g of P/ZSM-5 zeolite powder (80 mesh). No acid was used with thealumina. Water was sprayed to the alumina and zeolite mixture to form anextrudable paste which was extruded to make 1/16-inch cylindrical shapeextrudates. The bound catalyst was calcined in a convection oven in airat a maximum temperature between 510° C. to 530° C. (10 h) using thesame temperature profile as described for catalyst A. The catalyst B wascrushed and sized using 20 and 40 mesh screens for catalytic test. Usingthe same test conditions for catalyst A, catalyst B was tested fortoluene methylation and results are summarized in Table 4.

TABLE 4 Time on Stream, h 23.77 47.27 71.27 143.77 191.52 215.27 245.77Catalyst Bed Inlet Temp, ° C. 452.9 475.5 486.0 496.1 499.9 508.7 507.6Liquid Product Analysis, wt % Water 19.59 20.57 20.62 20.79 20.52 20.6820.74 Methanol 0.21 0.14 0.13 0.14 0.17 0.16 0.17 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 68.72 66.49 65.78 65.26 65.64 65.3365.19 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 9.23 10.67 11.32 11.70 11.5611.70 11.73 m-Xylene 0.85 0.89 0.92 0.92 0.89 0.90 0.89 o-Xylene 0.620.57 0.56 0.54 0.54 0.55 0.55 Ethyltoluenes 0.16 0.13 0.12 0.11 0.110.10 0.10 Trimethylbenzenes 0.56 0.54 0.55 0.55 0.57 0.58 0.62 C10+ 0.070 0 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 11.2412.86 13.48 13.98 13.74 13.83 13.97 Mixed Xylene Selectivity 94.06 95.4895.73 96.02 95.81 95.80 95.56 p-Xylene Selectivity 86.29 87.98 88.4488.91 88.99 88.96 89.09 Methanol Selectivity 51.28 58.08 60.63 62.7762.74 63.22 64.07

Example 3 Catalyst C

Synthesis of Catalyst C. Precalcined P-modified ZSM-5 (described asCatalyst A earlier) was bound with 20 wt % alumina binder. 17.5 g ofalumina (pseudobohemite type, available from Alcoa, HiQ-40 grade) wasmixed with 7.8 g HNO₃ (19.9 wt % in aqueous) and then mixed with 70.1 gof P/ZSM-5 zeolite powder (80 mesh). Water was sprayed on thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The bound catalyst wascalcined in a convection oven in air at a maximum temperature between510° C. to 530° C. (10 h) using the same temperature profile asdescribed for catalyst A. The catalyst C was crushed and sized using 20and 40 mesh screens for catalytic test. Using the same test conditionsfor catalyst A, catalyst C was tested for toluene methylation andresults are summarized in Table 5.

TABLE 5 Time on Stream, h 23.25 54.25 119.58 143.25 167.25 191.48 215.75Catalyst Bed Inlet Temp, ° C. 451.3 483.1 495.1 506.1 516.8 516.9 519.1Liquid Product Analysis, wt % Water 21.46 20.53 20.76 20.85 20.98 20.8520.99 Methanol 0.48 0.25 0.25 0.26 0.21 0.22 0.25 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 67.32 66.60 66.44 66.09 65.40 65.5165.27 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 8.64 10.77 10.86 11.15 11.6711.68 11.80 m-Xylene 0.71 0.69 0.65 0.64 0.68 0.68 0.66 o-Xylene 0.570.49 0.44 0.42 0.43 0.43 0.42 Ethyltoluenes 0.19 0.14 0.12 0.11 0.110.10 0.10 Trimethylbenzenes 0.55 0.54 0.49 0.49 0.52 0.51 0.50 C10+ 0.080 0 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 10.7812.51 12.57 12.87 13.11 13.33 13.38 Mixed Xylene Selectivity 93.47 95.4495.90 96.04 96.08 96.11 96.22 p-Xylene Selectivity 87.14 90.14 90.8991.34 91.32 91.27 91.58 Methanol Selectivity 52.19 59.57 59.89 61.4462.04 62.67 63.97

Example 4 Catalyst D

Synthesis of Catalyst D. Precalcined P-modified ZSM-5 (described asCatalyst A earlier) was bound with 20 wt % alumina binder. 17.5 g ofalumina (pseudobohemite type, available from Alcoa, HiQ-40 grade) wasmixed with 7.8 g HNO₃ (40.0 wt % in aqueous) and then mixed with 70.1 gof P/ZSM-5 zeolite powder (80 mesh). Water was sprayed to thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The bound catalyst wascalcined in a convection oven in air at a maximum temperature between510° C. to 530° C. (10 h) using the same temperature profile asdescribed for catalyst A. The catalyst D was crushed and sized using 20and 40 mesh screens for catalytic test. Using the same test conditionsfor catalyst A, catalyst D was tested for toluene methylation andresults are summarized in Table 6.

TABLE 6 Time on Stream, h 22.88 53.63 77.63 143.63 168.05 215.88 245.63Catalyst Bed Inlet Temp, ° C. 451.4 482.5 504.0 515.2 532.1 531.5 530.5Liquid Product Analysis, wt % Water 20.87 19.11 20.10 20.63 20.15 20.4420.24 Methanol 0.25 0.31 0.28 0.30 0.29 0.29 0.31 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 69.46 69.22 67.81 67.48 67.40 67.2967.47 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 8.31 10.16 10.63 10.47 11.0410.85 10.86 m-Xylene 0.37 0.42 0.42 0.42 0.43 0.43 0.43 o-Xylene 0.290.31 0.30 0.28 0.28 0.28 0.28 Ethyltoluenes 0.15 0.12 0.10 0.08 0.070.08 0.07 Trimethylbenzenes 0.30 0.35 0.35 0.33 0.34 0.34 0.34 C10+ 0 00 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 9.17 11.0811.64 11.41 11.72 11.63 11.63 Mixed Xylene Selectivity 95.89 96.52 96.7796.95 97.14 97.03 97.09 p-Xylene Selectivity 92.63 93.27 93.66 93.7693.95 93.88 93.89 Methanol Selectivity 45.11 55.24 57.50 57.28 59.1558.50 59.18

Example 5 Catalyst E

Synthesis of Catalyst E. Precalcined P-modified ZSM-5 (described asCatalyst A earlier) was bound with 20 wt % alumina binder. 17.5 g ofalumina (pseudobohemite type, available from Alcoa, HiQ-40 grade) wasmixed with 7.8 g HNO₃ (49.6 wt % in aqueous) and then mixed with 70.0 gof P/ZSM-5 zeolite powder (80 mesh). Water was sprayed to thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The bound catalyst wascalcined in a convection oven in air at a maximum temperature between510° C. to 530° C. (10 h) using the same temperature profile asdescribed for catalyst A. The catalyst E was crushed and sized using 20and 40 mesh screens for catalytic test. Using the same test conditionsfor catalyst A, catalyst E was tested for toluene methylation andresults are summarized in Table 7.

TABLE 7 Time on Stream, h 23.70 53.70 77.45 143.75 167.13 173.62 191.45Catalyst Bed Inlet Temp, ° C. 448.1 481.0 502.8 503.7 523.8 530.5 530.6Liquid Product Analysis, wt % Water 20.73 19.54 19.90 20.64 20.42 20.7020.74 Methanol 0.24 0.29 0.27 0.28 0.29 0.30 0.30 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 69.68 69.26 67.83 67.38 67.44 67.2367.38 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 8.38 9.84 10.92 10.65 10.8010.72 10.56 m-Xylene 0.32 0.38 0.41 0.39 0.42 0.42 0.40 o-Xylene 0.240.27 0.26 0.26 0.26 0.26 0.25 Ethyltoluenes 0.16 0.12 0.10 0.10 0.080.07 0.07 Trimethylbenzenes 0.25 0.30 0.30 0.29 0.30 0.30 0.29 C10+ 0 00 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 8.85 10.5011.83 11.53 11.45 11.37 11.14 Mixed Xylene Selectivity 96.10 96.72 97.1797.13 97.28 97.31 97.37 p-Xylene Selectivity 93.67 93.87 94.19 94.2594.10 94.08 94.19 Methanol Selectivity 43.34 52.29 58.23 58.46 58.0957.73 57.06

Example 6 Catalyst F

Synthesis of Catalyst F. Precalcined P-modified ZSM-5 (described ascatalyst A earlier) was bound with 20 wt % alumina binder. 17.5 g ofalumina (pseudobohemite type, available from Alcoa, HiQ-40 grade) wasmixed with 7.8 g HNO₃ (70.0 wt % in aqueous) and then mixed with 70.1 gof P/ZSM-5 zeolite powder (80 mesh). Water was sprayed to thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The bound catalyst wascalcined in a convection oven in air at a maximum temperature between510° C. to 530° C. (10 h) using the same temperature profile asdescribed for catalyst A. The catalyst F was crushed and sized using 20and 40 mesh screens for catalytic test. Using the same test conditionsfor catalyst A, Catalyst F was tested for toluene methylation andresults are summarized in Table 8.

TABLE 8 Time on Stream, h 23.05 46.80 71.30 143.30 167.32 191.30 215.05Catalyst Bed Inlet Temp, ° C. 454.2 475.6 495.0 505.7 517.5 516.4 516.1Liquid Product Analysis, wt % Water 20.50 20.37 20.17 20.29 20.20 20.1720.23 Methanol 0.41 0.48 0.47 0.54 0.56 0.57 0.57 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 70.88 69.90 69.60 69.88 70.17 70.1470.08 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 7.50 8.55 9.02 8.59 8.38 8.418.41 m-Xylene 0.21 0.22 0.24 0.24 0.24 0.24 0.24 o-Xylene 0.17 0.17 0.180.18 0.18 0.18 0.18 Ethyltoluenes 0.14 0.12 0.10 0.08 0.07 0.07 0.07Trimethylbenzenes 0.18 0.19 0.21 0.21 0.20 0.21 0.21 C10+ 0 0 0 0 0 0 0Conversion/Selectivity, mole % Toluene Conversion 7.66 8.78 9.53 8.548.14 8.69 8.58 Mixed Xylene Selectivity 96.53 97.08 97.32 97.23 97.3397.43 97.36 p-Xylene Selectivity 95.19 95.60 95.53 95.32 95.23 95.1995.16 Methanol Selectivity 41.74 48.33 52.36 50.76 48.74 51.77 50.73

Example 7

Catalyst G. An NH₄-ZSM-5 zeolite (SiO₂/Al₂O₃ mole ratio 280) was treatedwith H₃PO₄ by a wet impregnation method and then heated at a maximumtemperature of 550° C. Analyses of the P-treated ZSM-5 zeolite powderare shown in Tables 9 and 10. The P/ZSM-5 showed similar properties tothose of Catalyst A. Catalyst G was made using the P/ZSM-5 zeolitepowder and 20% alumina binder which had been prepared as follows: 25.0 gof alumina (pseudobohemite type, available from Alcoa, Hi/Q-40 grade)was mixed with 10.7 g HNO₃ (70.0 wt % in aqueous) and then mixed with100.0 g of P-treated zeolite powder (80 mesh). Water was sprayed on thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The extruded catalystwas calcined as described for catalyst A. Using the same test conditionsin example 1, Catalyst G was tested for toluene methylation and resultsare summarized in Table 11.

TABLE 9 Elemental Analysis, wt % N₂ Adsorption Si Al P SA, m²/g PV, ml/g35.38 0.30 9.72 188 0.15

TABLE 10 Powder XRD Intensity* d-spacing [A] Intensity 11.08 100 9.99 549.89 46 9.70 17 8.01 6 6.54 7 6.33 9 5.98 16 5.70 6 5.55 8 4.25 6 4.00 73.84 57 3.80 27 3.71 28 3.64 11 3.53 18 2.98 10 2.78 6 *Intensitiesshown are scaled in arbitrary units so that most intense peak is 100.

TABLE 11 Time on Stream, h 23.42 47.08 77.42 144.08 173.42 214.88 245.75Catalyst Bed Inlet Temp, ° C. 463.4 463.8 487.0 501.0 511.0 511.8 509.20Liquid Product Analysis, wt % Water 20.82 20.88 21.64 21.13 20.87 20.7920.70 Methanol 0.04 0.08 0.06 0.05 0.06 0.06 0.06 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 66.97 67.20 65.19 64.61 64.51 64.6864.60 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 11.49 11.14 12.39 12.84 13.8013.71 13.86 m-Xylene 0.24 0.24 0.27 0.29 0.30 0.30 0.31 o-Xylene 0.140.14 0.15 0.15 0.16 0.16 0.16 Ethyltoluenes 0.17 0.16 0.15 0.14 0.130.13 0.13 Trimethylbenzenes 0.14 0.15 0.16 0.16 0.17 0.17 0.18 C10+ 0 00 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 12.17 11.3613.26 14.30 14.86 14.64 14.80 Mixed Xylene Selectivity 97.84 97.64 98.0494.74 98.25 98.24 98.20 p-Xylene Selectivity 96.83 96.74 96.76 96.6996.79 96.79 96.74 Methanol Selectivity 54.01 51.43 59.13 62.95 66.0665.70 65.39

Examples 8-9 Clay Used as Matrix Catalysts H-I

Using the P-modified ZSM-5 powder (described as catalyst A) twocatalysts were formed using 10% alumina and 10% kaolin clay as bindermatrix.

Catalyst H: 8.75 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) and 8.75 g of kaolin clay (Aldrich) were mixed, andwere mixed with 7.8 g HNO₃ (19.9 wt % in aqueous) and then mixed with70.1 g of P/ZSM-5 zeolite powder (80 mesh). Water was sprayed to thezeolite-alumina mixture to form an extrudable paste which was extrudedto make 1/16-inch cylindrical shape extrudates. The bound catalyst wascalcined in a convection oven in air at a maximum temperature between510° C. to 530° C. (10 h) using the same temperature profile asdescribed for catalyst A. The catalyst H was crushed and sized using 20and 40 mesh screens for catalytic test. Using the same test conditions,catalyst H was tested for toluene methylation and results are summarizedin Table 12.

Catalyst I. 8.75 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) and 8.75 g of kaolin clay (Aldrich) were mixed with7.8 g HNO₃ (40.0 wt % in aqueous) and then mixed with 70.1 g of P/ZSM-5zeolite powder (80 mesh). Water was sprayed to the zeolite-aluminamixture to form an extrudable paste which was extruded to make 1/16-inchcylindrical shape extrudates. The bound catalyst was calcined in aconvection oven in air at a maximum temperature between 510° C. to 530°C. (10 h) using the same temperature profile as described for catalystA. The catalyst I was crushed and sized using 20 and 40 mesh screens forcatalytic test. Using the same test conditions in example 1, catalyst Iwas tested for toluene methylation and results are summarized in Table13.

TABLE 12 Time on Stream, h 22.75 46.68 76.93 142.77 173.85 215.48 245.53Catalyst Bed Inlet Temp, ° C. 452.6 475.7 506.2 518.1 521.5 523.8 523.9Liquid Product Analysis, wt % Water 19.34 19.26 19.94 19.48 19.07 18.9318.92 Methanol 0.31 0.29 0.24 0.22 0.25 0.27 0.27 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 71.33 69.61 67.30 67.38 67.64 67.6867.62 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 8.13 9.92 11.62 12.00 12.1312.21 12.27 m-Xylene 0.29 0.32 0.35 0.36 0.36 0.36 0.36 o-Xylene 0.230.22 0.21 0.21 0.21 0.21 0.22 Ethyltoluenes 0.15 0.12 0.10 0.10 0.090.09 0.09 Trimethylbenzenes 0.22 0.24 0.25 0.25 0.25 0.25 0.26 C10+ 0 00 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 8.73 10.6012.63 12.86 12.88 12.89 12.90 Mixed Xylene Selectivity 96.51 97.18 97.6697.75 97.78 97.80 97.79 p-Xylene Selectivity 94.04 94.76 95.37 95.4395.54 95.52 95.48 Methanol Selectivity 42.93 51.87 60.22 60.41 63.0362.30 63.05

TABLE 13 Time on Stream, h 29.23 53.40 77.40 149.40 191.23 215.15 245.40Catalyst Bed Inlet Temp, ° C. 464.5 483.9 505.3 517.2 530.9 531.7 531.2Liquid Product Analysis, wt % Water 21.06 19.90 20.70 19.67 19.42 19.9419.14 Methanol 0.27 0.30 0.32 0.38 0.35 0.36 0.38 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 68.73 68.98 68.01 69.33 69.66 69.3070.33 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 9.14 9.97 10.12 9.81 9.80 9.659.34 m-Xylene 0.27 0.30 0.30 0.31 0.30 0.28 0.29 o-Xylene 0.19 0.20 0.200.20 0.19 0.19 0.19 Ethyltoluenes 0.13 0.11 0.10 0.07 0.06 0.06 0.06Trimethylbenzenes 0.21 0.24 0.24 0.23 0.22 0.22 0.22 C10+ 0 0 0 0 0 0 0Conversion/Selectivity, mole % Toluene Conversion 9.72 10.58 10.56 10.069.82 9.67 9.30 Mixed Xylene Selectivity 97.11 97.27 97.41 97.58 97.7197.69 97.67 p-Xylene Selectivity 95.19 95.24 95.26 95.14 95.22 95.3595.12 Methanol Selectivity 48.49 52.69 53.99 54.01 52.76 52.57 51.01

Examples 10-12 Catalyst Made by Alumina Digestion Method Catalysts J-L

A P-modified ZSM-5 was made by following method described in U.S. Pat.No. 6,943,131 (Ghosh et al., 2005). 5.0 g alumina (pseudobohemite type,available from Alcoa, HiQ-40 grade) was dissolved in 100 ml water and67.04 g H₃PO₄ (85 wt % in aqueous) at temperature 70-80 ° C. The aluminasolution was added to a zeolite slurry containing 250.0 g NH₄ZSM-5(SiO₂/Al₂O₃ molar ratio 280) and 500 ml water at temperature 90-100° C.The zeolite slurry was stirred and was evaporated to dryness and themodified ZSM-5 was calcined using the temperature profile described forcatalyst A in preceding section. As described below, three catalystswere made by using the P-modified ZSM-5.

Example 10 (Comparative)

Catalyst J—The P-modified ZSM-5 (described above) was bound with 20 wt %alumina binder. 17.5 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) was mixed with 70.1 g of P/ZSM-5 zeolite powder (80mesh). No acid was used with the alumina. Water was sprayed to thealumina and zeolite mixture to form an extrudable paste which wasextruded to make 1/16-inch cylindrical shape extrudates. The boundcatalyst was calcined in a convection oven in air at a maximumtemperature between 510° C. to 530° C. (10 h) using the same temperatureprofile as described for catalyst A. The catalyst J was crushed andsized using 20 and 40 mesh screens for catalytic test. Using the sametest conditions in example 1, Catalyst J was tested for toluenemethylation and results are summarized in Table 14.

Example 11

Catalyst K—Precalcined P-modified ZSM-5 (described above) was bound with20 wt % alumina binder. 16.34 g of alumina (pseudobohemite type,available from Alcoa, HiQ-40 grade) was mixed with 7.27 g HNO₃ (40.0 wt% in aqueous) and then mixed with 65.4 g of P/ZSM-5 zeolite powder (80mesh). Water was sprayed to the zeolite-alumina mixture to form anextrudable paste which was extruded to make 1/16-inch cylindrical shapeextrudates. The bound catalyst was calcined in a convection oven in airat a maximum temperature between 510° C. to 530° C. (10 h) using thesame temperature profile as described for catalyst A. The catalyst K wascrushed and sized using 20 and 40 mesh screens for catalytic test. Usingthe same test conditions in example 1, catalyst K was tested for toluenemethylation and results are summarized in Table 15.

Example 12

Catalyst L. 37.8 g of alumina was mixed with 16.7 g HNO₃ (70.0 wt % inaqueous) and then mixed with 151.1 g of the modified ZSM-5 zeolitepowder (80 mesh). Water was sprayed to the zeolite-alumina mixture toform an extrudable paste which was extruded to make 1/16-inchcylindrical shape extrudates. The bound catalyst was calcined in aconvection oven in air at a maximum temperature between 510° C. to 530°C. using the same temperature profile as described for catalyst A. Thecatalyst L was crushed and sized using 20 and 40 mesh screens forcatalytic test. Using the same test conditions in example 1, catalyst Lwas tested for toluene methylation and results are summarized in Table16.

TABLE 14 Time on Stream, h 23.50 47.48 77.83 167.52 191.52 215.45 239.43Catalyst Bed Inlet Temp, ° C. 456.2 478.0 488.5 489.1 489.3 489.3 489.2Liquid Product Analysis, wt % Water 20.06 20.10 19.97 20.07 19.82 19.9419.74 Methanol 0.02 0 0 0 0 0 0 Dimethylether 0 0 0 0 0 0 0 Benzene 0 00 0 0 0 0 Toluene 68.09 66.78 66.20 65.76 65.79 65.63 65.74 Ethylbenzene0 0 0 0 0 0 0 p-Xylene 9.01 10.23 10.80 11.05 11.23 11.31 11.39 m-Xylene1.23 1.47 1.59 1.63 1.63 1.63 1.63 o-Xylene 0.75 0.71 0.74 0.77 0.770.77 0.77 Ethyltoluenes 0.19 0.16 0.15 0.14 0.13 0.13 0.13Trimethylbenzenes 0.59 0.55 0.56 0.58 0.59 0.59 0.60 C10+ 0.06 0 0 0 0 00 Conversion/Selectivity, mole % Toluene Conversion 11.94 13.29 13.9714.47 14.66 14.68 14.82 Mixed Xylene Selectivity 94.01 95.40 95.68 95.6895.74 95.74 95.75 p-Xylene Selectivity 82.03 82.44 82.24 82.17 82.4882.51 82.60 Methanol Selectivity 51.13 57.39 60.57 62.64 63.36 63.6564.04

TABLE 15 Time on Stream, h 23.10 47.10 77.90 143.65 167.55 191.90Catalyst Bed Inlet Temp, ° C. 452.1 464.8 478.8 481.0 481.6 481.6 LiquidProduct Analysis, wt % Water 19.69 19.54 20.06 19.54 19.76 20.31Methanol 0.03 0 0 0 0.01 0.01 Dimethylether 0 0 0 0 0 0 Benzene 0 0 0 00 0 Toluene 68.23 67.50 66.03 66.37 66.16 65.44 Ethylbenzene 0 0 0 0 0 0p-Xylene 9.84 10.61 11.53 11.69 11.70 11.88 m-Xylene 0.96 1.11 1.16 1.171.15 1.14 o-Xylene 0.56 0.57 0.57 0.58 0.57 0.57 Ethyltoluenes 0.18 0.180.15 0.15 0.15 0.14 Trimethylbenzenes 0.52 0.49 0.50 0.51 0.51 0.51 C10+0 0 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 12.0913.04 14.15 14.31 14.32 14.69 Mixed Xylene Selectivity 95.07 95.59 96.0496.07 96.09 96.17 p-Xylene Selectivity 86.64 86.34 86.96 87.00 87.2187.44 Methanol Selectivity 52.80 56.57 61.59 61.76 61.93 63.38

TABLE 16 Time on Stream, h 24.85 47.53 120.12 143.85 167.53 191.53222.35 Catalyst Bed Inlet Temp, ° C. 446.2 473.6 494.6 505.0 505.4 505.6505.0 Product Analysis, wt % Water 19.97 19.74 20.11 19.80 19.85 20.0320.11 Methanol 0.17 0.13 0.12 0.11 0.12 0.12 0.12 Dimethylether 0 0 0 00 0 0 Benzene 0 0 0 0 0 0 0 Toluene 70.41 68.17 66.63 66.36 66.23 65.8265.53 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 8.49 11.00 12.15 12.71 12.7812.99 13.18 m-Xylene 0.32 0.36 0.39 0.40 0.41 0.41 0.43 o-Xylene 0.240.23 0.23 0.23 0.23 0.23 0.24 Ethyltoluenes 0.17 0.14 0.12 0.11 0.110.11 0.12 Trimethylbenzenes 0.24 0.25 0.26 0.27 0.27 0.27 0.28 C10+ 0 00 0 0 0 0 Conversion/Selectivity, mole % Toluene Conversion 9.42 12.1013.41 14.08 14.06 14.32 14.62 Mixed Xylene Selectivity 96.36 97.27 97.5597.67 97.68 97.67 97.64 p-Xylene Selectivity 93.84 94.97 95.18 95.2795.28 95.27 95.20 Methanol Selectivity 44.34 56.00 61.54 64.33 64.8265.73 64.99

TABLE 17 PX Selectivity Over Various P-ZSM-5 Catalysts g HNO3/ PXSelectivity Catalyst Binder g Binder^(a) (mole %) A No binder 88.53 B20% Al₂O₃ 0 88.91 C 20% Al₂O₃ 0.089 91.58 D 20% Al₂O₃ 0.178 93.84 E 20%Al₂O₃ 0.220 94.15 F 20% Al₂O₃ 0.311 95.19 G 20% Al₂O₃ 0.311 96.76 H 10%Al₂O₃ (+10% Kaolin) 0.089 95.16 I 10% Al₂O₃ (+10% Kaolin) 0.178 95.22J^(b) 20% Al₂O₃ 0 82.41 K^(b) 20% Al₂O₃ 0.178 87.20 L^(b) 20% Al₂O₃0.311 95.28 ^(a)Binder or binder plus kaolin; ^(b)PZSM-5 made by Aldigestion method

Examples 13-16 (Comparative) Catalysts M-N

Synthesis of Catalysts M-N. Zeolite H-ZSM-5 (SiO₂/Al₂O₃ molar ratio 280)powder was bound with alumina to make two catalysts—one without mixingalumina with nitric acid and the other with mixing alumina with nitricacid. The zeolites were not modified with phosphorus.

Example 13

Catalyst M: 25.0 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) was mixed with 100.1 g of the HZSM-5 zeolite powder(80 mesh). Water was sprayed to the alumina and zeolite mixture whichwas extruded to make 1/16-inch cylindrical shape extrudates.

Example 14

Catalyst N: 20.2 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) was mixed with 8.97 g HNO₃ (70.0 wt % in aqueous)and then mixed with 80.6 g of the HZSM-5 zeolite powder (80 mesh). Waterwas sprayed to the zeolite-alumina mixture to form an extrudable pastewhich was extruded to make 1/16-inch cylindrical shape extrudates.

Both extruded catalysts were calcined in a convection oven in air at amaximum temperature between 510° C. to 530° C. (10 h) using the sametemperature profile as described for catalyst A. The catalysts werecrushed and sized using 20 and 40 mesh screens for catalytic test. Usingthe same test conditions in example 1, Catalysts M and N were tested fortoluene methylation and results are summarized in Tables 18 and 19,respectively.

TABLE 18 Time on Stream, h 23.32 47.33 77.87 143.28 173.88 198.08 245.57Catalyst Bed Inlet Temp, ° C. 453.7 464.4 463.7 474.9 472.5 473.2 472.5Liquid Product Analysis, wt % Water 20.28 19.86 20.11 20.18 20.00 19.6820.03 Methanol 0 0 0 0 0 0 0 Dimethylether 0 0 0 0 0 0 0 Benzene 0 0.160.12 0.13 0.10 0.09 0.08 Toluene 66.00 66.03 65.83 65.75 66.01 66.4766.21 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 3.07 3.23 3.34 3.42 3.56 3.583.68 m-Xylene 6.47 6.59 6.43 6.43 6.22 6.11 5.99 o-Xylene 2.68 2.74 2.712.72 2.64 2.61 2.56 Ethyltoluenes 0.74 0.55 0.47 0.36 0.36 0.33 0.33Trimethylbenzenes 0.66 0.74 0.86 0.91 0.97 0.98 0.99 C10+ 0.11 0.11 0.130.12 0.14 0.14 0.14 Conversion/Selectivity, mole % Toluene Conversion13.70 14.05 14.08 14.26 13.86 13.74 13.68 Mixed Xylene Selectivity 90.0289.53 89.36 89.87 90.07 89.67 90.18 p-Xylene Selectivity 25.13 25.7026.74 27.20 28.64 29.14 30.10 Methanol Selectivity 55.25 56.46 56.8857.81 56.57 55.94 55.88

TABLE 19 Time on Stream, h 23.23 47.48 71.23 142.98 173.23 197.23 244.55Catalyst Bed Inlet Temp, ° C. 449.9 441.2 440.1 442.5 453.7 460.3 469.2Liquid Product Analysis, wt % Water 20.60 21.23 21.00 21.26 20.91 19.5219.65 Methanol 0 0 0 0 0 0 0 Dimethylether 0 0 0 0 0 0 0 Benzene 0.230.12 0.10 0.08 0.09 0.10 0.10 Toluene 64.02 64.68 65.05 65.08 65.2266.02 65.80 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 3.38 3.17 3.22 3.41 3.463.65 3.69 m-Xylene 7.22 6.49 6.37 6.07 6.20 6.50 6.59 o-Xylene 3.03 2.702.65 2.55 2.61 2.72 2.75 Ethyltoluenes 0.71 0.76 0.73 0.58 0.50 0.430.39 Trimethylbenzenes 0.71 0.73 0.76 0.85 0.90 0.93 0.92 C10+ 0.11 0.110.11 0.12 0.12 0.13 0.11 Conversion/Selectivity, mole % TolueneConversion 15.36 14.25 14.05 13.29 13.40 14.31 14.01 Mixed XyleneSelectivity 88.47 88.26 88.67 88.42 89.41 89.72 90.67 p-XyleneSelectivity 24.81 25.66 26.30 28.36 28.20 28.35 28.32 MethanolSelectivity 60.32 55.75 55.58 52.29 53.87 57.24 56.56

Catalysts O-P

Synthesis of Catalysts O and P. Zeolite NH₄-ZSM-5 (SiO₂/Al₂O₃ molarratio 700) powder was bound with alumina to make two catalysts—onewithout mixing alumina with nitric acid and the other with mixingalumina. The zeolites were not modified with phosphorus.

Example 15

Catalyst 0: 17.5 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) was mixed with 70.0 g of the NH₄ZSM-5 zeolitepowder (80 mesh). Water was sprayed to the alumina and zeolite mixtureand was extruded to make 1/16-inch cylindrical shape extrudates.

Example 16 Example 16

Catalyst P: 17.5 g of alumina (pseudobohemite type, available fromAlcoa, HiQ-40 grade) was mixed with 7.79 g HNO₃ (70.0 wt % in aqueous)and then mixed with 70.1 g of the NH₄ZSM-5 zeolite powder (80 mesh).Water was sprayed to the zeolite-alumina mixture to form an extrudablepaste which was extruded to make 1/16-inch cylindrical shape extrudates.

Both extruded catalysts were calcined in a convection oven in air at amaximum temperature between 510° C. to 530° C. (10 h) using the sametemperature profile as described for catalyst A. The catalysts werecrushed and sized using 20 and 40 mesh screens for catalytic test. Usingthe same test conditions in example 1, Catalysts O and P were tested fortoluene methylation and results are summarized in Tables 20 & 21respectively.

TABLE 20 Time on Stream, h 23.58 53.58 119.58 143.58 173.58 197.83221.58 Catalyst Bed Inlet Temp, ° C. 446.9 479.10 483.9 495.1 497.6494.4 494.4 Product Analysis, wt % Water 21.15 20.35 21.01 20.60 19.6220.37 20.33 Methanol 0 0 0 0 0 0 0 Dimethylether 0 0 0 0 0 0 0 Benzene 00.05 0.05 0.05 0.05 0 0.05 Toluene 66.11 65.62 65.08 64.97 65.72 64.9465.09 Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 5.62 5.80 6.15 6.51 7.06 7.437.47 m-Xylene 4.16 4.80 4.57 4.72 4.56 4.32 4.23 o-Xylene 1.77 2.12 2.022.04 1.96 1.88 1.82 Ethyltoluenes 0.32 0.11 0.08 0.07 0.07 0.07 0.07Trimethylbenzenes 0.77 0.94 0.93 0.91 0.91 0.90 0.86 C10+ 0.10 0.11 0.100.09 0.09 0.08 0.07 Conversion/Selectivity, mole % Toluene Conversion12.62 13.78 13.85 14.28 14.47 14.56 14.42 Mixed Xylene Selectivity 91.9891.95 92.74 93.07 93.37 93.87 93.63 p-Xylene Selectivity 48.68 45.5548.23 49.05 52.12 54.50 55.25 Methanol Selectivity 51.59 56.85 57.6459.64 60.84 61.57 60.82

TABLE 21 Time on Stream, h 24.38 52.88 119.88 143.22 173.88 198.02221.88 Catalyst Bed Inlet Temp, ° C. 449.2 495.7 502.7 503.3 495.7 496.7500.7 Product Analysis, wt % Water 20.20 18.40 20.24 20.17 21.11 17.9520.86 Methanol 0 0 0 0 0 0 0 Dimethylether 0 0 0 0 0 0 0 Benzene 0 0.060.06 0 0 0 0 Toluene 66.44 66.31 64.95 64.71 64.74 65.98 64.28Ethylbenzene 0 0 0 0 0 0 0 p-Xylene 5.31 6.13 6.25 7.03 7.35 7.93 7.45m-Xylene 4.84 5.43 5.01 4.73 4.41 4.59 4.19 o-Xylene 1.99 2.34 2.21 2.142.08 2.17 1.97 Ethyltoluenes 0.31 0.18 0.14 0.08 0.08 0.09 0.08Trimethylbenzenes 0.81 1.03 1.03 1.04 1.09 1.17 1.07 C10+ 0.10 0.12 0.110.11 0.12 0.13 0.11 Conversion/Selectivity, mole % Toluene Conversion13.02 14.71 14.57 14.99 14.16 15.51 14.76 Mixed Xylene Selectivity 92.2491.95 92.08 93.06 98.19 92.60 92.69 p-Xylene Selectivity 43.70 44.1346.39 50.59 53.09 54.00 54.75 Methanol Selectivity 53.55 60.41 60.0862.45 62.82 63.98 61.08

As shown in the data above, the combination of a phosphorus-modifiedZSM-5 with alumina or clay binder material which has been treated withnitric acid in a catalyst for a process of methylation of tolueneresults in improved selectivity to p-xylene. The comparative exampleswithout binder (Example 1), without treatment of the binder with mineralacid (Examples 2 and 10), without phosphorus modification of the zeolite(Examples 13-16) show lower selectivity to p-xylene than a catalyst of aphosphorus-modified ZSM-5 with alumina or clay binder material which hasbeen treated with nitric acid (Examples 3-9, 11 and 12). FIG. 1 showsthe difference in p-xylene selectivity for a bound P-modified ZSM-5without (Example 2, Catalyst B) and with (Example 6, Catalyst F)treatment of the binder with mineral acid. FIG. 2 shows the lack ofeffect on p-xylene selectivity for a bound ZSM-5 without phosphorusmodification and without (Example 13, Catalyst M) and with (Example 14,Catalyst N) treatment of the binder with mineral acid.

The crush strength using a flat plate method was measured for calcined1/16-inch extrudates of Catalyst B (Example 2 Comparative without acidtreatment of the binder), Catalyst C, Catalyst D and Catalyst F(Examples 3, 4 and 6 with acid treatment of the binder). The averagecrush strength is shown in Table 22.

TABLE 22 Average Crush Catalyst Strength (lb/mm) B 2.10 C 3.36 D 3.41 F3.68

As shown in the data above, the combination of a phosphorus-modifiedZSM-5 with alumina or clay binder material which has been treated withnitric acid results in improved crush strength. The comparative exampleof a phosphorus-modified ZSM-5 with alumina binder material which hasnot been treated with nitric acid (Catalyst B) shows lower average crushstrength than P-ZSM-5 catalysts having alumina binder material which hasbeen treated with nitric acid (Catalysts C, D and F). Higher crushstrength indicates that such catalyst should have less physicalattrition of the catalyst and longer catalyst life in processconditions.

Obviously, numerous modifications and variations of the presentinvention are possible in light of the above teachings. It is thereforeto be understood that within the scope of the appended claims, theinvention may be practiced otherwise than as specifically describedherein.

1-43. (canceled)
 44. A method of preparing an alkyl aromatic productcomprising: a) treating a zeolite containing 10-oxygen ring pores with aphosphorus compound to form a phosphorus-treated zeolite; b) treating aninorganic oxide binder material with a mineral acid; c) combining thephosphorus-treated zeolite with an inorganic oxide binder material toform a zeolite-binder mixture; d) heating the zeolite-binder mixture attemperature of about 400° C. or higher to form a bound zeolite catalyst;and e) contacting the bound zeolite catalyst with an aromatic alkylationfeed of an aromatic compound and an alkylating agent under reactionconditions suitable for aromatic alkylation.
 45. The method of claim 44wherein the binder material includes at least one of alumina, clay,aluminum phosphate and silica-alumina.
 46. The method of claim 44wherein the binder material is an alumina-containing material.
 47. Themethod of claim 44 wherein the binder material is present in an amountof from about 1% to about 99% by weight of the bound zeolite catalyst.48. The method of claim 44 wherein the binder material contains fromabout 1% to 99% by weight alumina or clay or their combinations.
 49. Themethod of claim 44 wherein the zeolite is a ZSM-5 zeolite.
 50. Themethod of claim 44 wherein the phosphorus-treated zeolite is heated to atemperature of about 300° C. or higher.
 51. The method of claim 44wherein the zeolite-binder mixture is heated to a temperature of from400° C. to about 700° C.
 52. The method of claim 44 further comprisingadding water to the zeolite-binder mixture and shaping thezeolite-binder mixture
 53. The method of claim 44 wherein the aromaticcompound is toluene.
 54. The method of claim 44 wherein the aromaticcompound is toluene and the alkylating agent is methanol.
 55. The methodof claim 44 further comprising steaming the bound zeolite at atemperature of 300° C. or less prior to contacting with the aromaticalkylation feed.
 56. The method of claim 44 wherein the zeolite istreated with a phosphorus compound to form a phosphorus-treated zeolitehaving a phosphorus content of from 0.01 to about 0.15 gram ofphosphorus per gram of zeolite.
 57. The method of claim 56 wherein thezeolite is a ZSM-5 zeolite.
 58. The method of claim 57 wherein thebinder material includes at least one of alumina, clay, aluminumphosphate and silica-alumina.
 59. The method of claim 57 wherein thebinder material is an alumina-containing material.
 60. The method ofclaim 57 wherein the binder material is present in an amount of fromabout 1% to about 99% by weight of the bound ZSM-5 zeolite catalyst. 61.The method of claim 57 wherein the binder material contains from about1% to 99% by weight alumina.
 62. The method of claim 57 wherein thephosphorus-treated ZSM-5 zeolite is heated to a temperature of about300° C. or higher.
 63. The method of claim 56 wherein the zeolite-bindermixture is heated to a temperature of from 400° C. to about 700° C. 64.The method of claim 54 further comprising steaming the bound ZSM-5zeolite at a temperature of 300° C. or less prior to contacting with thefeed of toluene.
 65. The method of claim 44 wherein the mineral acid ishydrochloric acid, nitric acid, phosphoric acid or sulfuric acid
 66. Themethod of claim 65 wherein the mineral acid is nitric acid.